FENAPOL UP 13157-15
Brookfield viscosity at 25°C: 400 – 500 TIX index: 13 – 16 Gel time at 25°C: 13 – 16 Exothermic Peak: 160 – 180 Peak Time: 7 – 11 Styrene content: 37 – 39 HDT: 72 Tensile elongation: 2 Type: ortho Notes: Not pre accelerated
FENAPOL UP 13343-30
Brookfield viscosity at 25°C: 700 – 800 TIX index: 25 -35 Gel time at 25°C: 25 -35 Exothermic Peak: 165 – 200 Peak Time: 10am – 4pm Styrene content: 38 – 41 HDT: 90 Tensile elongation: 2.2 Type: Iso NPG Notes: Not pre accelerated
FENAPOL UP 14150 A 10
Brookfield viscosity at 25°C: 1500 – 2000 TIX index: 7 – 10 Gel time at 25°C: 7 – 10 Exothermic Peak: 140 – 160 Peak Time: 10 – 12 Styrene content: 29 – 31 HDT: 95 Tensile elongation: 2.5 Type: Ortho Notes: Pre accelerated with amine for mastics
FENAPOL UP 18100-5
Brookfield viscosity at 25°C: 600 – 700 TIX index: 3 – 6 Gel time at 25°C: 3 – 6 Exothermic Peak: 205 – 225 Time to Peak: 5 – 8 Styrene content: 34 – 38 HDT: 90 Tensile elongation: 2.5 Type: Ortho Notes: High performance
FENAPOL UP 18714 RZ
Brookfield viscosity at 25°C: 250 – 350 TIX index: 3 – 8 Gel time at 25°C: 3 – 8 Exothermic Peak: 210 – 230 Time to Peak: 5 – 10 Styrene content: 34 – 36 HDT: 110 Tensile elongation: 1.5 Type: DCPD Notes: High performance, low viscosity
FENAPOL UP 18940 FS
Brookfield viscosity at 25°C: 500 – 600 TIX index: 3 – 6 Gel time at 25°C: 3 – 6 Exothermic Peak: 205 – 235 Time to Peak: 5 – 8 Styrene content: 37 – 39 HDT: 100 Tensile elongation: 4.5 Type: ISO NPG Notes: Flexible, light stabilized
FENAPOL UP 17713-20
Brookfield viscosity at 25°C: 250 – 350 TIX index: 14 – 20 Gel time at 25°C: 14 – 20 Exothermic Peak: 165 – 185 Time to Peak: 6 – 10 Styrene content: 32 – 34 HDT: 70 Tensile elongation: 2 Type: Ortho DCPD Notes: Non-pre accelerated with low styrene content for flat laminates with gelcoat
NORESTER 6811
Brookfield viscosity at 25°C: 250 – 450 TIX index: 15 – 25 Gel time at 25°C: 15 – 25 Exothermic Peak: 145 – 165 Time to Peak: 20 – 30 Styrene content: 42 – 48 HDT: 105 Tensile elongation: 5.6 Type: VE Notes: For chemically resistant products. Application for FW. Certifications The resins are produced […]
ADICROL FD 315 S
Field of use Particularly suitable for the production of adhesives for laminates. Acids/Anhydrides: Aromatic Main glycols: DEG Structure: linear Appearance: liquid OH number: 300 – 330 mg KOH/g Acid Number: ≤ 1.5 mg KOH/g Brookfield viscosity (temperature): 2000 – 3000 (25°C) mPa s Water content: ≤ 0.10% Hazen color: ≤ 250
ADISOL AIP 75 AE 75 (75% solido in acetato di etile)
Field of use Used in the formulation of solvent-based adhesives Acids/Anhydrides: Aromatic / Aliphatic Main glycols: MPG, 1,4-BDO Structure: branched Appearance: liquid OH number: 70 – 80 mg KOH/g Acid Number: ≤ 8 mg KOH/g Brookfield viscosity (temperature): 3000 – 4000 (25°C) mPa s Water content: ≤ 0.1% Hazen color: ≤ 250